主 题:A Superalloys C High-temperature oxidation C Grain boundaries oxidation
摘 要:Chromia forming Alloy 718 and AD730TM have been submitted to isothermal long-term air exposure up to 10 000 h at 700 degrees C. The resulting very low specific mass gain led to consider two alternatives to determine the oxidation kinetics. Measurements of the external layer thickness and of the intergranular oxide amount were carried out on SEM micrographs evidencing the intergranular oxidation contribute around 30% to the total specific mass change. AD730TM with a thicker external scale and a higher amount of intergranular oxide showed a twofold faster oxidation rate than Alloy718. The results demonstrated the need of even longer tests.