Enhanced mechanical properties of Mg-3Al-1Zn alloy sheets through slope extrusion

作     者：Huabao Yang Yanfu Chai Bin Jiang Chao He Junjie He Qingshan Yang Ming Yuan Huabao Yang;Yanfu Chai;Bin Jiang;Chao He;Junjie He;Qingshan Yang;Ming Yuan

作者机构：School of Mechanical and Electrical EngineeringShaoxing UniversityShaoxing 312000China Tianjin Key Laboratory of Composite&Functional MaterialsSchool of Materials Science and EngineeringTianjin UniversityTianjin 300072China State Key Laboratory of Mechanical TransmissionsCollege of Materials Science and EngineeringChongqing UniversityChongqing 400044China College of Materials Science and EngineeringYunnan UniversityKunming 650091China School of Metallurgy and Material EngineeringChongqing University of Science and TechnologyChongqing 401331China 

出 版 物：《International Journal of Minerals,Metallurgy and Materials》 (矿物冶金与材料学报（英文版）)

年 卷 期：2022年第29卷第7期

页      面：1343-1350页

核心收录：

学科分类：08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

基　　金：financially supported by the National Natural Science Foundation of China (Nos. U1764253, 51971044, 51901204, U1910213 52001037, and U207601) the National Defense Basic Scientific Research Program of China, the Chongqing Science and Technology Commission, China (No.cstc2017zdcy-zdzxX0006) the Chongqing Municipal Education Commission, China (No.KJZDK202001502) the Chongqing Scientific & Technological Talents Program, China (No.KJXX2017002) the Qinghai Scientific & Technological Program, China (No.2018-GXA1) the Zhejiang Provincial Natural Science Foundation, China (No.LGG21E050009) the Research Start-up Funds of Shaoxing University, China (No.20210007) 

主　　题：AZ31 Mg alloy sheets slope extrusion microstructure texture strength 

摘      要：A novel extrusion approach,entitled slope extrusion(SE),was employed to manufacture AZ31(Mg-3Al-1 Zn,wt%)alloy *** microstructures,textures,and mechanical properties were investigated,compared with those of the AZ31 sheet fabricated by conventional extrusion(CE).Through the combination of finite element simulation and actual experiment,the ultimate results indicated that significant grain refinement(from 9.1 to 7.7 and 5.6μm)and strong basal texture(from 12.6 to 17.6 and 19.5 mrd)were achieved by the SE *** essence was associated with the additional introduced inclined interface in the process of SE,which could bring about more asymmetric deformation and stronger accumulated strain along the ND when compared with the process of *** a consequence,the SE sheets exhibited a higher yield strength(YS)and ultimate tensile strength(UTS)than the counterparts of the CE sheet,which was mainly assigned to the synergistic effects from grain refining and texture strengthening.