Microstructure,wear and friction behavior of CoCrAITaY-xCNTs composite coatings deposited by laser-induction hybrid cladding

作     者：Sheng-Feng Zhou Yu Long Yan-Liang Yi Cheng Deng Lian-Xi Hu Sheng-Feng Zhou;Yu Long;Yan-Liang Yi;Cheng Deng;Lian-Xi Hu

作者机构：Institute of Advanced Wear&Corrosion Resistant and Functional MaterialsJinan UniversityGuangzhou510632China Wuhan National Laboratory for Optoelectronics(WNLO)Huazhong University of Science and TechnologyWuhan430074China MOE Key Laboratory of New Processing Technology for Non-Ferrous Metals and MaterialsGuangxi Key Laboratory of Processing for Non-Ferrous Metals and Featured MaterialsGuangxi UniversityNanning530004China School of Mechatronics EngineeringGuangdong Polytechnic Normal UniversityGuangzhou510635China School of Materials Science and EngineeringHarbin Institute of TechnologyHarbin150001China 

出 版 物：《Rare Metals》 (稀有金属（英文版）)

年 卷 期：2024年第43卷第4期

页      面：1815-1827页

核心收录：

学科分类：080503[工学-材料加工工程] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0802[工学-机械工程] 080201[工学-机械制造及其自动化] 

基　　金：financially supported by the National Natural Science Foundation of China(Nos.52005217 and 51261026) the Basic and Applied Basic Research Fund Project of Guangdong Province in China(Nos.2023A1515012684,2021A1515010523 and 2020A1515110020) the University Research Platform and Research Projects of Guangdong Education Department(No.2022ZDZX3003) the Open Foundation of Guangxi Key Laboratory of Processing for Non-ferrous Metals and Featured Materials(No.2022GXYSOF18) Guanxi Key Laboratory of Information Materials(No.221012-K) the Open Project Program of Wuhan National Laboratory for Optoelectronics(No.2021WNLOKF010) the Fundamental Research Funds for the Central Universities(No.21622110) 

主　　题：Carbon nanotube MCrAlY coating Friction and wear performance Laser-induction hybrid cladding 

摘      要：To improve the wear performance of CoCrAlYTa coating,part of the carbon nanotubes(CNTs)chemically reacted with Ta to form reinforcement phase(TaC),while the other CNTs were retained as lubrication ***,the CoCrAlYTa-xCNTs(x=0,1,2,and 4;wt%)composite coatings were prepared by laserinduction hybrid cladding(LIHC),and the microstructure and wear resistance of coatings were systematically *** show that the coatings are mainly composed of TaC,y-(Co,Cr)andβ-(Co,Cr)*** the CNTs content increases from 0 wt%to 4 wt%,the volume fraction of TaC increases from 13.11 vol%to 16.12 vol%.Meanwhile,the nano-hardness ofγ-(Co,Cr)andβ-(Co,Cr)Al are improved from 7.49 and 9.72 to 9.36 and 11.19 GPa,*** a result,the microhardness of coating increases from HV536.25 to HV 738.16,the wear rate decreases from32.4×10^(-3)to 6.1×10^(-3)mg·m^(-1),and the average friction coefficient decreases from 0.55 to *** good wear performance of the coating is attributed to the formation of TaC and the existence of remained CNTs lubricant film.