Dry Methane Reforming Performance of Ni-based Catalyst Coated onto Stainless Steel Substrate

作     者：Suntorn Sangsong Monrudee Phongaksorn Sabaithip Tungkamani Thana Sornchamni Rungroj Chuvaree 

作者机构：Department of Industrial Chemistry Faculty of Applied Science King Mongkut's University of Technology North Bangkok Bangkok 10800 Thailand Research and Development Center for Chemical Engineering Unit Operation and Catalyst Design (RCC) King Mongkut's University of Technology North Bangkok Bangkok 10800 Thailand PTT Public Company Limited PTT Research and Technology Institute Ayutthaya 13170 Thailand 

出 版 物：《Energy Procedia》 

年 卷 期：2015年第79卷

页      面：137-142页

主　　题：Nickel Based Catalysts Spray Coating Dry Methane Reforming 

摘      要：In this work, the Ni-based catalysts (10 wt.%Ni/Al 2 O 3 -MgO and 10 wt.%Ni/MgO) were synthesized by sol-gel method. Each catalyst was prepared as catalyst pellets and catalyst-coated plate, stainless steel plate coated with catalyst. The catalyst-coated plates were fabricated using spray coating. The dry methane reforming (DMR) performances of catalyst-coated plate were investigated and compared with DMR performances of catalyst pellets. As the mass transfer was improved, the methane consumption rate per gram of catalyst coated onto metal plate was ten times greater than those of catalyst pellets approximately. The carbon deposition was also significantly prevented when the catalyst was constructed as a thin-film layer on the plate under our developing condition. Therefore, this catalyst-coated plate can be further developed for multichannel reactor.