The Structure and Emission Properties of SiO_2 Nanometer Film Containing Ag

作     者：张兆艳 

作者机构：Sch. of Material Sci. and Technology Wuhan University of Technology Wuhan 430070 China 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2001年第16卷第2期

页      面：34-37页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

主　　题：silica film silver emission intensity 

摘      要：Colloidal silver particles are formed on float glass by heat treatment with coated silica film containing Ag by sol-gel process . The Sn2+ on surface of float glass influences the formation of colloidal Ag particles . The microstructure of the film and the granularity of silver particles were studied by TEM and HEED. The emission property of the samples was measured. The results show that aggregation of metal particles degrades emission intensity , and that content of Ag, withdrawing speed and heat treatment temperature of samples has a greater effect on photoluminescence.