TC4 micro-arc oxidation(MAO)coatings were prepared by adding SiO_(2) nanoparticles or sodium silicate to the sodium meta-aluminate-based *** effect of additives was investigated by XRD,SEM,EDS,electrochemical and wear...
详细信息
TC4 micro-arc oxidation(MAO)coatings were prepared by adding SiO_(2) nanoparticles or sodium silicate to the sodium meta-aluminate-based *** effect of additives was investigated by XRD,SEM,EDS,electrochemical and wear *** results show that additives can considerably accelerate the formation of MAO *** coatings are mostly composed of rutile and anatase TiO_(2),α-Al_(2)O_(3),γ-Al_(2)O_(3),Al_(2)TiO_(5) and SiO_(2).Sodium silicate and SiO_(2) nanoparticles added to the coating can effectively reduce the size of micropores and increase its thickness,whereas SiO_(2) nanoparticles with superior physical properties can be directly deposited at the discharge channel,significantly increasing the coating's resistance to wear and *** coating with SiO_(2) nanoparticles exhibits the best overall performance,with the lowest corrosion rate and average friction coefficient of 4.095×10^(-5)mm/a and 0.30,respectively.
暂无评论