A series of H3PO4-modified CeO2 samples were prepared by impregnation of CeO2 with H3PO4solution,and evaluated for the selective catalytic reduction of NOx by *** samples were characterized by X-ray diffraction,N2 ads...
详细信息
A series of H3PO4-modified CeO2 samples were prepared by impregnation of CeO2 with H3PO4solution,and evaluated for the selective catalytic reduction of NOx by *** samples were characterized by X-ray diffraction,N2 adsorption-desorption,infrared spectroscopy,Raman spectroscopy,X-ray photoelectron spectroscopy,temperature-programmed desorption of NH3,and temperature-programmed reduction of *** results showed that more than 80%NO conversion was achieved in the temperature range 250-550℃ over the H3PO4-CeO2 *** enhanced catalytic performance could be ascribed to the increase in acidic strength,especially Bronsted acidity,and reduction in redox properties of the CeO2 after H3PO4 modification.
建立了一种利用气相色谱(GC)检测1,3-环戊二酮化合物去对称对映选择性还原反应转化率和产物含量的方法,作为一种重要辅助手段,用于磷中心手性膦酰胺催化环状1,3-二酮类化合物的去对称对映选择性还原反应机理的研究。样品经DB-WAX色谱柱(30 m×0.25 mm, 0.25μm)分离,以标准化合物比对的方法,采用GC进行定性及定量分析,可简便、快速、准确测定在不同反应时间剩余原料和生成的不同产物的量。采用本方法对无添加剂和催化剂、只加入添加剂、只加入催化剂以及同时加入添加剂和催化剂4种情况下的反应进程进行了检测。结果表明,相比其它3种反应体系,同时加入添加剂N,N-二异丙基乙胺(DIPEA)和催化剂的反应体系的原料转化速度快,在5 min内反应转化率达到80%以上,单还原目标产物的含量接近70%。对照实验结果表明,加入DIPEA可大幅提高产物的对映选择性。本研究结果有助于深入理解相关反应的机理,即胺类添加剂的加入可促进手性活性催化物种的生成。
富勒烯稠合噁唑啉衍生物的合成已建立多种方法,但绝大多数方法仅限于芳香族类底物.发展了一种N,N-二甲基甲酰胺(DMF)促进富勒烯C60与酰胺类底物在碱性条件下合成富勒烯稠合噁唑啉的方法,该方法对脂肪族和芳香族酰胺均具有较好的兼容性,能以27%~62%的收率成功合成了一系列富勒烯稠合噁唑啉衍生物.实验结果表明N,N-二甲基甲酰胺(DMF)在此反应中作为共溶剂,可以显著提高目标化合物的收率.现场可见近红外吸收光谱和对照实验研究表明,富勒烯稠合噁唑啉二负离子是反应的关键中间体,DMF有利于此二负离子的生成并对此二负离子起到稳定作用.电化学性质研究显示,富勒烯稠合噁唑啉产物的噁唑啉环上不含取代基和含芳基取代基的衍生物,其起始还原电位相对于C60无明显变化,但噁唑啉环上含脂肪烷基的衍生物的起始还原电位有较大负移,达到0.1 V.
暂无评论