The hot deformation behavior of a high Ti 6061 aluminum alloy in the temperature range from 350 to 510 ℃ and strain rate range from 0.001 to 10 s^-1 was investigated using stress-strain curve analysis, processing map...
详细信息
The hot deformation behavior of a high Ti 6061 aluminum alloy in the temperature range from 350 to 510 ℃ and strain rate range from 0.001 to 10 s^-1 was investigated using stress-strain curve analysis, processing map, transmission electron microscopy and electron backscatter diffraction analysis. The results show that the peak stress decreases with increasing deformation temperatures and decreasing strain rate. The average deformation activation energy is 185 kJ/mol in the parameter range investigated. The flow stress model was constructed. The main softening mechanism is dynamic recovery. The processing map was obtained using dynamic material model, and the suggested processing window is 400-440℃ and 0.001-0.1 s^-1.
Based on the elastoplastic mechanical properties of the weld and heat affected zone metals obtained by a nanoindentation test, a theoretical calculation model was established for the forming limit diagram（FLD） of ta...
详细信息
Based on the elastoplastic mechanical properties of the weld and heat affected zone metals obtained by a nanoindentation test, a theoretical calculation model was established for the forming limit diagram（FLD） of tailor-welded blanks（TWBs） on the basis of plastic constitutive relations and Hosford yield criteria. Hemispherical punch bulging tests were performed to verify the FLD theoretical calculation results. The results demonstrated that not only the FLD theoretical calculation of base materials but also that of TWBs had a good agreement with their experiments. Besides, poorer formability of TWBs caused its FLD significantly lower than that of base materials. The theoretical calculation model offers a reliable approach to obtain the specific FLD of TWBs.
暂无评论