A green synthetic route is reported for quickly synthesis of highly luminescent CdTe-Mn/ZnS quantum dots (QDs) in aqueous solution. Glutathione (GSH) was used as capping reagent and thioacetamide (TAA) as sulfur sourc...
详细信息
Rod-like β-Ga2O3:Dy3+ blue/yellow phosphors doped with different concentration of Dy3+ were synthesized by the rapid microwave hydrothermal and calcination method. Although the crystallization of β-Ga2O3:Dy3+ sample...
详细信息
Rod-like β-Ga2O3:Dy3+ blue/yellow phosphors doped with different concentration of Dy3+ were synthesized by the rapid microwave hydrothermal and calcination method. Although the crystallization of β-Ga2O3:Dy3+ samples decreased as the Dy3+ concentration increasing, the samples' morphology maintained and were not influenced by the Dy3+ concentration under XRD and SEM characterizations. Photoluminescence measurement results showed that the emission peaks of β-Ga2O3:Dy3+ phosphors located at 492 nm (blue) and 580 nm (yellow), the intensity of blue/yellow emission varied with Dy3+ concentrations and showed a maximum when the concentration of Dy3+ at 3mol%, the corresponding blue/yellow ratio was 59.29%/40.71%. In addition, the probable mechanisms of GaOOH growth and Dy3+ doping into GaOOH:Dy3+ and β-Ga2O3:Dy3+ were analyzed briefly.
GaOOH precursors with different morphologies and sizes were synthesized by hydrothermal method. The products were characterized by XRD, SEM and the probable growth mechanism of GaOOH was analyzed. The pH values played...
详细信息
GaOOH precursors with different morphologies and sizes were synthesized by hydrothermal method. The products were characterized by XRD, SEM and the probable growth mechanism of GaOOH was analyzed. The pH values played a dominated role in adjusting GaOOH morphologies and had an effect on their crystallizations. The GaOOH precursors were calcined in air and transformed into α-Ga2O3 and β-Ga2O3 under 600°C and 900°C, respectively. The samples after calcinations showed coincident morphology hereditability. Photoluminescence measurements(λex=250 nm) were conducted for the GaOOH and Ga2O3 samples and the emission peaks located at 415 nm and 465 nm when pH=5, however, at 370 nm and 465 nm for pH=3 and 8.
Radiofrequency low temperature plasma was used to mutate the strain B8 which can adsorb nickel ions, and the adsorptive ability of the mutant was tested. The experiments show that the optimum mutagenic conditions of B...
详细信息
Radiofrequency low temperature plasma was used to mutate the strain B8 which can adsorb nickel ions, and the adsorptive ability of the mutant was tested. The experiments show that the optimum mutagenic conditions of B8 by plasma are as follows: the mutation time of 3 min, the mutation power of 50~65 W, the carrier gas of N2 and the carrier gas pressure of 20 Pa. The mutant Ni12 with high adsorptive ability was screened from the mutant strains of B8 mutated under above conditions, and the nickel ion adsorption capacity of the mutant Ni12 reaches 136.7 mg · g-1 (dry bacteria), which is 11.7% higher than that of raw strain B8. The genetic stability of mutant Ni12 can maintain in 5 generations. The mechanism study shows that the extra cellular polymer is an important factor affecting the adsorption of nickel ions. After the formation of mutant Ni12 biofilm on the porous ceramics, from solution with nickel ion concentration of 50 mg · L-1, the nickel ion adsorption ratio of Ni12 reaches 86%. The result of 16S rDNA sequence analysis indicates that the mutant Ni12 is Pseudomonas cedrina. The advantage of mutagenesis of raw strain B8 by radiofrequency low temperature plasma is its high efficiency, and the inheritance of mutant strain Ni12 is stable. Therefore, it has promising prospect of using it to treat the wastewater containing nickel ions.
Nanogold particles in different sizes, from 5 to 60 nm, were utilized to modify the surface of the quartz crystal microbalance (QCM). It was found that the gold-particle size of the modified QCM affects both the amoun...
Nanogold particles in different sizes, from 5 to 60 nm, were utilized to modify the surface of the quartz crystal microbalance (QCM). It was found that the gold-particle size of the modified QCM affects both the amount of the immobilization of the probe on the surface of QCM and the hybridization rate of the target DNA. 20 nm was determined to be the optimal size for the surface modification and it can maximally increase the sensitivity of the DNA detection.
Using the chemical bath deposition for aqueous solution containing zinc acetate and ammonium hydroxide, the phase composition and morphology of samples, soluble Zn ion concentration in the mother liquid at different a...
详细信息
Using the chemical bath deposition for aqueous solution containing zinc acetate and ammonium hydroxide, the phase composition and morphology of samples, soluble Zn ion concentration in the mother liquid at different aging time were studied. The results indicated that octahedrally microcrystals of the stable intermediate Ε-Zn(OH)2 were produced at early stages under these conditions. Transformation from Ε-Zn(OH)2 to ZnO was observed to occur at various aging time. Transformation from Ε-Zn(OH)2 to ZnO followed two mechanisms: dissolution-reprecipitation and solid-solid phase transformation mechanism.
ZnO nanorod arrays were firstly grown on FTO conducting glass via a simple chemical bath deposition method, then ZnO nanorod arrays/nanoparticles aggregate composite films were obtained by sequential growth of ZnO nan...
详细信息
ZnO nanorod arrays were firstly grown on FTO conducting glass via a simple chemical bath deposition method, then ZnO nanorod arrays/nanoparticles aggregate composite films were obtained by sequential growth of ZnO nanorod arrays. The dye-covered ZnO electrodes, Pt counter electrode and electrolyte solution were assembled into dye-sensitized solar cells (DSSCs). Due to their relatively high surface area, fast electron transport, and enhanced light-scattering capability, a short current density(Jsc) of 11.7 mA/cm2, an open-circuit voltage (Voc) of 0.661 V, a fill factor(FF) of 0.384, and overall solar-to-electric energy conversion efficiency of 3.17% were achieved for the ZnO nanorod arrays/nanoparticles aggregate composite films DSSCs under sunlight illumination with AM1.5 (100 mW/cm2), which were much higher than those obtained for the monodisperse aggregate DSSCs and ZnO nanorod array DSSCs.
AZ91 alloy was prepared by cold pressing and sintering using AZ91 alloy powders after ball milling. Microstructure of the specimens sintered at different temperatures was studied by means of optical microscope (OM) an...
详细信息
AZ91 alloy was prepared by cold pressing and sintering using AZ91 alloy powders after ball milling. Microstructure of the specimens sintered at different temperatures was studied by means of optical microscope (OM) and scanning electronic microscopy(SEM). The hardness of as-cast sample and the sample sintered at 600°C was tested by micro-hardness tester. The results show that the irregular powder particles change from several hundreds microns into 9.98 μm in size, and become uniform in morphology after ball milling. With sintering temperature increasing, the relative density of the alloy increases obviously due to the enhancement of diffusion ability of elements and the change of sintering mechanism from solid phase sintering to liquid phase sintering. When sintering temperature reaches 600°C, the relative density is 96.3%, the hardness of specimen prepared by powder metallurgy increases obviously, from 81.06 HV of the as-cast alloy to 104.39 HV.
A novel kind of supramolecular polymer filament with a diameter of 2–5 µm was artificially synthesized, which is in fact a bundle of self-assembled nanotubes with a diameter of about 40 nm. The filament can be d...
详细信息
A novel kind of supramolecular polymer filament with a diameter of 2–5 µm was artificially synthesized, which is in fact a bundle of self-assembled nanotubes with a diameter of about 40 nm. The filament can be drawn from a special alkaline aqueous solution directly and free standing in room temperature, which has never been performed earlier. A microtensile tester was developed with the aid of an electronic balance to investigate the mechanical properties of the new filament. Monotonic and load–unload tensile tests were performed, respectively. The maximum tensile strength and the elastic modulus of the filament were 23.8 MPa and 1.9 GPa, respectively, which were higher than previous supramolecular polymers and comparable to some covalent-linked polymers.