The precursor of M-type barium hexaferrite with iron excess, which the nominal composition was BaFe12.4O19.6, was prepared by a so-called co-dump coprecipitation method. The crystallization behavior of the precursor u...
详细信息
The precursor of M-type barium hexaferrite with iron excess, which the nominal composition was BaFe12.4O19.6, was prepared by a so-called co-dump coprecipitation method. The crystallization behavior of the precursor under the spark plasma sintering (SPS) conditions and the magnetic properties of the SPS samples were investigated. The results show that the samples obtained at 700-850°C were composed of single-phase M-type barium hexaferrite, and that the crystallization of intermediates such as BaFe2O4 and Y-Fe2O3 did not occur. The distribution of crystal grains obviously changed with the increase of temperature;the distribution was random at 700°C and became preferential orientation when the temperature was more than 700°C. The saturation magnetization significantly increased at 700°C and remained almost constant in the range of 750°C to 850°C. This accorded with the evolution characteristics of the phase composition of the SPS samples with the increase of temperature. The coercivity first increased and then decreased with the increase of the temperature, which was attributed to the corresponding increases in the content of M-type barium ferrite and the degree of preferential orientation of crystal grains.
The carbonyl iron/Al2O3 core-shell composite particles with different morphologies of nanoshells were prepared and the influences of the Al2O3 nanoshell morphologies on the properties of the carbonyl iron/Al2O3 core-s...
详细信息
The carbonyl iron/Al2O3 core-shell composite particles with different morphologies of nanoshells were prepared and the influences of the Al2O3 nanoshell morphologies on the properties of the carbonyl iron/Al2O3 core-shell composite particles were investigated. The results show that the shell morphologies of the carbonyl iron/Al2O3 core-shell composite particles strongly depend on the species of acid and pH value. Compared to the carbonyl iron particles, the anti-oxidation property, microwave electromagnetic parameters and mechanical properties of the composite particles are significantly improved, and the particles, uniform, compact and grain-like Al2O3 nanoshells are beneficial to improving the anti-oxidation property and decreasing permittivity with the retention of permeability, while fiber-like Al2O3 nanoshells are more advantageous to improving the interface compatibility between the particles and the matrix of the polymers, resulting in obvious increase of mechanical properties of their based absorbing coatings.
Tin dioxide based ceramics doped with ZnO, Sb2O3 and ZnO-Sb2O3 were prepared by the pressureless sintering. The relative density (ρr) was measured by the Archimedes method, the resistivity (R) was measured by the van...
详细信息
Tin dioxide based ceramics doped with ZnO, Sb2O3 and ZnO-Sb2O3 were prepared by the pressureless sintering. The relative density (ρr) was measured by the Archimedes method, the resistivity (R) was measured by the van der Pauw method, and the mi-crostructure and crystal structure were measured by scanning electron microscope. Then the internal relationship between the material and structure were analyzed. The results indicate that ZnO can improve the sintering characteristics of the material;the ρr increases and then decreases with the increase of ZnO, and the optimal content of ZnO is 1.0% (mole fraction, the same below). However, the ρr decreases with the increase of Sb2O3;the R decreases at first, and then increases and decreases at last. The ρr and R of the material are good when Sb2O3 content is 0.5%. The SnO2 based ceramic doped with 1.0% ZnO-0.5% Sb2O3 and sintered at 1400°C has high performance;the ρr is 97% and the R is 0.1099 Ω·cm.
Pulse current heating technology is used to join TiB2-Ni cermets with Ti6A14V at different temperatures (1023K, 1073K and 1123K) with 7MPa pressure and Cu foil and Ni foil are used as joining interlayer. Joint points ...
详细信息
Pulse current heating technology is used to join TiB2-Ni cermets with Ti6A14V at different temperatures (1023K, 1073K and 1123K) with 7MPa pressure and Cu foil and Ni foil are used as joining interlayer. Joint points increase with welding temperature. The microstructure of joints is observed through SEM images and micrographs. The diffusion coefficient (D0) of Cu at the Cu/TiB2 interface is calculated by the EPMA patterns. The diffusion principle of pulse current heating and influences of electric field and current on atom diffusion are studied.
Ga dopping GaxPb1-xTe(x=0.01-0.05) compounds were prepared by melting reaction method, and the in-c fluence of Ga content on the thermoelectric properties were investigated. The results showed that temperature dopende...
详细信息
Ga dopping GaxPb1-xTe(x=0.01-0.05) compounds were prepared by melting reaction method, and the in-c fluence of Ga content on the thermoelectric properties were investigated. The results showed that temperature dopendent carrier concentration increased and the hall mobility decreased with increasing Ga content, which indicated that the carrier scattering mechanism gradually changed from an acoustical scattering to the interaction between an acoustical phone and an ionized impurity scattering as x increased. All samples show n-type conduct and the absolute Seebeck coefficient values and the electric conductivity increase significantly with increasing Ga content.
The layered perovskite-type organic-inorganic hybrids (CnH2n+1NH3)2 MnCl4 (n=2, 4, 6, 8, 10, 12) were synthesized in solution and their structures were characterized. The results showed that the structures of the prod...
详细信息
The layered perovskite-type organic-inorganic hybrids (CnH2n+1NH3)2 MnCl4 (n=2, 4, 6, 8, 10, 12) were synthesized in solution and their structures were characterized. The results showed that the structures of the products were independent on the reaction initial temperature. The X-ray diffraction (XRD) patterns and the scanning electron microscopy (SEM) images of the products demonstrated that the hybrids crystallize very well and had typical layered structures. The interlayer distance of each hybrid was obtained from the XRD patterns. It was linear dependent on the carbon atom number in the organic chain and the organic chains interdigitated between the two adjacent inorganic sheets.
The solubility of layered perovskite-type organic-inorganic hybrids (CnH2n+1 NH3)2MCl4 (where M = Mn, Co, Cu, Zn;n = 2, 4, 6, 8, 10, 12) in seven kinds of solvent are obtained by atomic absorption spectrometry and tit...
详细信息
The solubility of layered perovskite-type organic-inorganic hybrids (CnH2n+1 NH3)2MCl4 (where M = Mn, Co, Cu, Zn;n = 2, 4, 6, 8, 10, 12) in seven kinds of solvent are obtained by atomic absorption spectrometry and titration method. The solvents are sherwood oil, cyclohexane, acetone, trichloromethane, DMF, methanol and water. The results show that the hybrids are prone to dissolve in polar solvent. This is attributed to the polarity of the hybrids. The hybrids disassembly dissolve when the interaction between the ammonium and the electron-donating group of the solvent is stronger than that between the organic and the inorganic parts in the hybrids. The series of M = Zn and Co have better solubility in the polar solvent than that of M = Mn and Cu and this is presumably because there are weaker interactions between the organic and inorganic parts in hybrids of M = Zn and Co.
Using a reticulated polyurethane sponge with interconnected pores as primal framework and immersing into TiB2 slurry consisting of Ni and Mo as sintering additives, a porous TiB2 ceramics with high porosity and interc...
详细信息
Using a reticulated polyurethane sponge with interconnected pores as primal framework and immersing into TiB2 slurry consisting of Ni and Mo as sintering additives, a porous TiB2 ceramics with high porosity and interconnected pores was prepared by immersing and high temperature sintering process. The rheology of TiB2slurry which used silica sol as a binder was studied. The optimum condition of the slurry suitable for impregnating the polyurethane sponge was obtained. The flexural strength of the porous reticulated TiB2 ceramics can reach 1 MPa.
Based on the empirical electron theory (EET) of solids and molecules, the valence electron structures (VESs) of TiC-Mo(Ni)-Fe system were calculated by building proper structure model. The results indicate that additi...
详细信息
Based on the empirical electron theory (EET) of solids and molecules, the valence electron structures (VESs) of TiC-Mo(Ni)-Fe system were calculated by building proper structure model. The results indicate that additives of Mo and Ni improve the interface conjunction factors of the cermets in different ways. By adding Mo, the VESs of the ceramic phase are improved for the formation of the rim phase (Ti1-xMox)C, which leads to the enhancement of the interface conjunction, while the improvement of the VESs on metal phase by adding Ni is due to the formation of the Fe100-yNiy. Mo and Ni additives increase the interface electron density of cermets, that is, the adding of the Mo and Ni enhance the overlapping grade of the electron cloud on interface and increase the binding energy of the interface, which is propitious to the wettability. The best wettability was found at x=0.5 or y=30.
Sodium potassium bismuth titanate (KNBT) slurry with high plasticity was prepared by the viscous polymer processing. The effects of milling time, bonding agent content, dispersant content, and pH value on the rheologi...
详细信息
Sodium potassium bismuth titanate (KNBT) slurry with high plasticity was prepared by the viscous polymer processing. The effects of milling time, bonding agent content, dispersant content, and pH value on the rheological properties were investigated by rheograms, and the optimal technological parameters were investigated. The KNBT fibers with improved properties were fabricated via an extruding machine. The results show that the slurry has optimal rheological behavior when the milling time is 16 h, the pH value is 7, the bonding agent content is 1.22% (in mass, the same below), and the dispersant content is 0.4%.