BaCO3 whiskers exhibiting different morphologies were fabricated by a simple precipitation reaction of barium ch/oride with sodium carbonate in the absence and presence of poly-（styrene-alt-maleic acid） （PSMA） as ...
详细信息
BaCO3 whiskers exhibiting different morphologies were fabricated by a simple precipitation reaction of barium ch/oride with sodium carbonate in the absence and presence of poly-（styrene-alt-maleic acid） （PSMA） as a crystal growth modifier at room temperature. The as-prepared products were characterized by scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, and X-ray diffraction （XRD）. The influences of experimental parameters on the size and morphology of BaCO3 whiskers were investigated and discussed. It was found that the as-prepared BaCO3 whiskers are single crystals with diameter ranging from 100 to 300 run, and grow along the crystallographic a-axis or [100] direction. BaCO3 whiskers with different morphologies, such as branching and dendritic structure, can be obtained depending on the experimental conditions. With increasing PSMA concentration, the diameter of BaCO3 whiskers decreases.
Novel ordered mesoporous Eu(DBM)3phen/APTES-SBA-15 (EAS) composites with reasonable photoluminescence property and interesting morphology of bundles of pearl-like chains were synthesized. The characteristics of the me...
详细信息
Novel ordered mesoporous Eu(DBM)3phen/APTES-SBA-15 (EAS) composites with reasonable photoluminescence property and interesting morphology of bundles of pearl-like chains were synthesized. The characteristics of the mesostructure and the optical properties of the prepared samples were investigated by means of XRD, FTIR, SEM, TEM, N2 adsorption–desorption and PL spectroscopy. The results indicate that the as-made EAS composites have long-distance ordered mesoporous structure. Compared with the Eu(DBM)3phen complex, it is found that the EAS composites perform a considerable photoluminescence with good color purity. It is proposed that the anchored amine from the APTES and quantum size effect of the Eu(DBM)3phen complex have great effect on the photoluminescence of the EAS composites.
Ordered iron fiber arrays were electrodeposited on the surface of zinc foils using ＂FeSO4 solution-sodium caprylate-Decanol＂ 3-component reverse hexagonal liquid crystal as soft templates. The structure of the soft ...
详细信息
Ordered iron fiber arrays were electrodeposited on the surface of zinc foils using ＂FeSO4 solution-sodium caprylate-Decanol＂ 3-component reverse hexagonal liquid crystal as soft templates. The structure of the soft templates and the synthesized iron ,fibers were characterized by polarizing microscopy, X-ray diffraction （XRD）, scanning electron microscopy （SEM） and energy dispersive X-ray microanalysis etc. The experimental results shou that the synthesized iron fibers with a crystal phase grew up in the form of fiber clusters of about 200 nm along the direction perpendicular to the cathode surface. Each cluster was composed of several tens of fibers. The fibers had almost the same length of more than 10μm with a diameter of about 50 nm.
Pulse current heating (PCH) was used to join Ti-6Al-4V alloy at two cases of with die and without die. Hot-pressing (HP) method was used to provide a comparison between the two methods. Microstructures near the contac...
详细信息
Pulse current heating (PCH) was used to join Ti-6Al-4V alloy at two cases of with die and without die. Hot-pressing (HP) method was used to provide a comparison between the two methods. Microstructures near the contacting surfaces were observed in optical microscope. Temperature distribution was analyzed. After joining, the tensile properties of the samples were evaluated. Experimental results show that grains and phases grow transversely on contacting surfaces, which makes two parts into a whole with a certain of tensile strength. PCH joining is a different temperature joining method. The highest temperature is located at the interface. The comparison of tensile strengths of samples joined by the two methods indicates that joining temperature and holding time needed by PCH are lower and less than those needed for HP.
Rhizama Chuanxiong is a kind of traditional medicinal herb used to promote blood circulation and eliminate wind to relieve pain. In this work, nano Rhizoma Chuanxiong particles were successfully prepared by high speed...
详细信息
Rhizama Chuanxiong is a kind of traditional medicinal herb used to promote blood circulation and eliminate wind to relieve pain. In this work, nano Rhizoma Chuanxiong particles were successfully prepared by high speed centrifugal sheering (HSCS) pulverizer. The influence of processing parameters on the size of Rhizama Chuanxiong particles and the different properties between nano Rhizoma Chuanxiong particles and original fine powder were systematically studied by ZetaPALS light scattering granulometric analyzer and optical microscope. The content of effective ingredient tetramethylpyrazine (TMP) was determined by high-performance liquid chromatography (HPLC). The results illustrate that general Rhizama Chuanxiong powder can be ultrafinely ground to nanometer within 50 min, and the cellular tissues of Rhizoma Chuanxiong are broken into pieces and dispersed stably and homogeneously after being ultrafinely ground. In addition, the active ingredients can dissolve out directly and fully, and the extraction ratio of TMP is increased 32.2% by HSCS processing.
Samples of LiNi0.95-xCoxAl0.05O2 （x = 0.10 and 0.15） and LiNiO2, synthesized by the solid-state reaction at 725℃ for 24 h from LiOH-H2O, Ni2O3, Co2O3, and AI（OH）3 under an oxygen stream, were characterized by TG-...
详细信息
Samples of LiNi0.95-xCoxAl0.05O2 （x = 0.10 and 0.15） and LiNiO2, synthesized by the solid-state reaction at 725℃ for 24 h from LiOH-H2O, Ni2O3, Co2O3, and AI（OH）3 under an oxygen stream, were characterized by TG-DTA, XRD, SEM, and electrochemical tests. Simultaneous doping of cobalt and aluminum at the Ni-site in LiNiO2 was tried to improve the cathode performance for lithium-ion batteries. The results showed that co-doping （especially, 5 at.% A1 and 10 at.% Co） definitely had a large beneficial effect in increasing the capacity （186.2 mA.h/g of the first discharge capacity for LiNio.s.42OoaoAlo.0502） and cycling behavior （180.1 mA-h/g after 10 cycles for ***2） compared with 180.7 mA.h/g of the first discharge capacity and 157.7 mA.h/g of the tenth discharge capacity for LiNiO2, respectively. Differen- tial capacity versus voltage curves showed that the co-doped LiNio.95_***2 had less intensity of the phase transitions than the pristine LiNiO2.
Three novel dielectric ceramics Ba5LnZnNb9O30 (Ln= La, Nd and Sm) were synthesized and characterized in the BaO-Ln2O3-ZnO-Nb2O5 quaternary system, which formed the filled tungsten-bronze structures. The present cerami...
详细信息
Three novel dielectric ceramics Ba5LnZnNb9O30 (Ln= La, Nd and Sm) were synthesized and characterized in the BaO-Ln2O3-ZnO-Nb2O5 quaternary system, which formed the filled tungsten-bronze structures. The present ceramics exhibit high dielectric constant (εr) up to 310, low dielectric loss in the level of 10 3 at 1 MHz. Meanwhile, the temperature coefficients of the dielectric constant (τε) of Ba5LnZnNb9O3o varies from -1 390×10-6 to -1 220×10-6/℃as the radius of Ln3+ increases. The present ceramics are promising candidates for high dielectric constant and low loss dielectric ceramics.
A kind of p-type segmented Bi2 Te3/CoSB3 thermoetectric material was preparea oy sparse ptasma sintering（ SPS ） . When the segmented materials were used at the temperature ranging from 300 K to 800 K, the junction t...
详细信息
A kind of p-type segmented Bi2 Te3/CoSB3 thermoetectric material was preparea oy sparse ptasma sintering（ SPS ） . When the segmented materials were used at the temperature ranging from 300 K to 800 K, the junction temperature was optimized, which is about 500 K, and the corresponding length ratio of CoSb3 to Bi2 Te3 is about 15 ： 2. The measured maximum power output of segmented materials is abont 320 W·m^-2, which is about 1.8 times as high as that of monolithic material CoSb3 under the same measuring conditions.
Porous alumina of regular spherical particles was fabricated with the spark plasma sintering （SPS） and then compared to those obtained through conventional hot pressing （HP）. The effects of the parameters of the h...
详细信息
Porous alumina of regular spherical particles was fabricated with the spark plasma sintering （SPS） and then compared to those obtained through conventional hot pressing （HP）. The effects of the parameters of the heating process on porosity were also investigated, Microstructural studies suggest that porous ingots including regular pores be made out of regular spherical alumina particles due to the close sphere packages. A comparative study on the relative necks of the specimens produced by SPS and HP indicates an enhancement of neck growth with SPS. Contrasting the theoretical values to the experimental results over the relative necks indicates that a proper relationship between the relative necks and the porosity can be established by a sintering model.
The microwave magnetic properties of the ball milled FeCo panicles were investigated as functions of ball milling time （ t ） using microwave electromagnetic parameters analysis techniques. The results show that the ...
详细信息
The microwave magnetic properties of the ball milled FeCo panicles were investigated as functions of ball milling time （ t ） using microwave electromagnetic parameters analysis techniques. The results show that the imaginary part of intrinsic dynamic permeability （ ui ） of the ball- milled panicles is much bigger than that of raw powders. ui strongly depends on t and exhibits several slightly damped ferromagnetic resonances. These phenomena are in qualitative agreement with the formation of the corresponding microstructure or the Aharoni ＇ s model of non-uniform exchange resonance modes. The present microwave permeabilhy behavior indicates that nanocrystalline materials with the same grain size may exhibit different properties that depend upon the microstructure, which provides a possibility for manufacturing high performance microwave absorber.