A kind of p-type segmented Bi2 Te3/CoSB3 thermoetectric material was preparea oy sparse ptasma sintering（ SPS ） . When the segmented materials were used at the temperature ranging from 300 K to 800 K, the junction t...
详细信息
A kind of p-type segmented Bi2 Te3/CoSB3 thermoetectric material was preparea oy sparse ptasma sintering（ SPS ） . When the segmented materials were used at the temperature ranging from 300 K to 800 K, the junction temperature was optimized, which is about 500 K, and the corresponding length ratio of CoSb3 to Bi2 Te3 is about 15 ： 2. The measured maximum power output of segmented materials is abont 320 W·m^-2, which is about 1.8 times as high as that of monolithic material CoSb3 under the same measuring conditions.
Porous alumina of regular spherical particles was fabricated with the spark plasma sintering （SPS） and then compared to those obtained through conventional hot pressing （HP）. The effects of the parameters of the h...
详细信息
Porous alumina of regular spherical particles was fabricated with the spark plasma sintering （SPS） and then compared to those obtained through conventional hot pressing （HP）. The effects of the parameters of the heating process on porosity were also investigated, Microstructural studies suggest that porous ingots including regular pores be made out of regular spherical alumina particles due to the close sphere packages. A comparative study on the relative necks of the specimens produced by SPS and HP indicates an enhancement of neck growth with SPS. Contrasting the theoretical values to the experimental results over the relative necks indicates that a proper relationship between the relative necks and the porosity can be established by a sintering model.
The PAn-PEO-PAn triblock copolymer with the PEG chain length of 400 was synthesized by chemical oxidation copolymerization of aniline and α,ω-bis（p-aminophenyl）poly（ethylene glycol）and characterized by FT-IR and...
详细信息
The PAn-PEO-PAn triblock copolymer with the PEG chain length of 400 was synthesized by chemical oxidation copolymerization of aniline and α,ω-bis（p-aminophenyl）poly（ethylene glycol）and characterized by FT-IR and *** experimental results show that the copolymer particles are of μtypical core-shell structure after the self-assembly process in *** conductivity is much lower than that of the pure *** suspension containing 20 vol% PAn-PEO-PAn tiblock copolymer in silicone oil exhibits.a typical electrorheological （ER） effect in DC electric *** it shows a lower leakage current density than that of the pure PAn-based ER ***,the PEO shell hinders the electric hop among PANI chains and decreases the current density of ER fluids in an external electric *** the same time the interface polarity improves the ER effects.
The microwave magnetic properties of the ball milled FeCo panicles were investigated as functions of ball milling time （ t ） using microwave electromagnetic parameters analysis techniques. The results show that the ...
详细信息
The microwave magnetic properties of the ball milled FeCo panicles were investigated as functions of ball milling time （ t ） using microwave electromagnetic parameters analysis techniques. The results show that the imaginary part of intrinsic dynamic permeability （ ui ） of the ball- milled panicles is much bigger than that of raw powders. ui strongly depends on t and exhibits several slightly damped ferromagnetic resonances. These phenomena are in qualitative agreement with the formation of the corresponding microstructure or the Aharoni ＇ s model of non-uniform exchange resonance modes. The present microwave permeabilhy behavior indicates that nanocrystalline materials with the same grain size may exhibit different properties that depend upon the microstructure, which provides a possibility for manufacturing high performance microwave absorber.
TiAl/Ti2AlC composites were prepared by in-situ hot pressing of TilAl/C powders mixtures and sintered at different temperatures were investigated by X- ray diffraction （ XRD ） of samples. The reaction procedure of T...
详细信息
TiAl/Ti2AlC composites were prepared by in-situ hot pressing of TilAl/C powders mixtures and sintered at different temperatures were investigated by X- ray diffraction （ XRD ） of samples. The reaction procedure of Ti-Al-C system could be divided into three stnges. Below 900℃ , Ti reacts with Al to form TiAl intermetallics ; above 900 ℃ , C reacts with remain Ti to form TiC triggered by the exothermal reaction of Ti and Al ; TiAl reacts with TiC to produce dense TiAl/Ti2AlC *** the holding stage, ternary Ti2AlC develops to layered polycrystal and composites pyknosis in the meanwhile. The mechanism of synthesis and microstructure was especially discussed.
The temperature field during the whole process of SPS sintering TiB2 -BN sample was numerically simulated based on the simplification of the temperature rising process. The result shows that the highest temperature is...
详细信息
The temperature field during the whole process of SPS sintering TiB2 -BN sample was numerically simulated based on the simplification of the temperature rising process. The result shows that the highest temperature is found in the punch and the heat flows from punch to sample and die in SPS sintering system. In the radial direction, the center temperature of the sample is much higher than the circumference temperature of the sampie. In the axial direction, the center temperature of the sample is lower than the border temperature of the sampie. The temperature difference in the sample is growing bigger in the sintering process and reaches the maximum at the end of the heating-up process.
The spark plasma sintering （SPS） was applied to prepare α-Si3 N4 ceramics of different densities with magnesia, silicon dioxide, alumina as the sintering aids. The mechanism of liquid phase sintering （LPS） wus d...
详细信息
The spark plasma sintering （SPS） was applied to prepare α-Si3 N4 ceramics of different densities with magnesia, silicon dioxide, alumina as the sintering aids. The mechanism of liquid phase sintering （LPS） wus discussed and the factors influencing the density of the prepared samples were analyzed. The dielectric constant of sintered samples was tested. The experimental results show that the density can be controlled from 2.48 g/ cm^3 to 3.09 g/ cm^3 while the content of the sintering aids and the sintering temperature alter and the dielectric constant is closely dependent on the density of obtained samples.
A new niobate Ba6Mg0.67Nb9.33O30 was ssnthesized in the BaO-MgO-Nb2O5 system by solid state reaction at 1350 ℃ for 48 b. The strncture and dielectric properties of Ba6Mg0.67Nb9.33O30 were determined by X-ray pouder d...
详细信息
A new niobate Ba6Mg0.67Nb9.33O30 was ssnthesized in the BaO-MgO-Nb2O5 system by solid state reaction at 1350 ℃ for 48 b. The strncture and dielectric properties of Ba6Mg0.67Nb9.33O30 were determined by X-ray pouder diffraction, straining electron microscopy and dielectric measurements. The results show that Ba6Mg0.67Nb9.33O30 belongs to ferroelectric phase of filled tetragonal tungsten bronze structure at room temperature with unit cell parameters ： a = 1. 26052（4） nm , c = 0.40045（2） nm, space group P4bm , calculated density 5 . 707g. cm ^-3 . Ba6Mg0.67Nb9.33O30 belongs to relaxor ,ferroetectrics undergoing diffusive phase transition, and the transition temperature （ Tc ） is 30 ℃ observed at 10 kHz. At room temperature, Ba6Mg0.67Nb9.33O30 eeramic has a high dielectric constant 850 at 1 MHz and a low dielectric loss of 0. 0052.
In order to improve the bioavailability, Radix salvia miltiorrhiza raw powder mixed with distilled water （5.5wt%） was ultrafinely ground to nanosize particles using HSCS pulverizer, and the dissolving-out quantity o...
详细信息
In order to improve the bioavailability, Radix salvia miltiorrhiza raw powder mixed with distilled water （5.5wt%） was ultrafinely ground to nanosize particles using HSCS pulverizer, and the dissolving-out quantity of tanshinone IIA in the filtrate that obtained from nanoparticles suspension and raw powder marinated in water for different time was determined by HPLC. The experimental results show that raw powder can be ultrafinely ground to 133.5 nm at 1500 r/min for 50 min and the molecular structure of active ingredients doesnot change, and the dissolving-out quantity of tanshinone IIA obtained from the filtrate is increased greatly from 12.77 μg/g to 54.55 μg/g.
A facile modification strategy is developed to promote the proliferation and osteogenic differentiation of rat bone marrow stromal cells(rBMSCs)through deposition of a bioactive calcium silicate(CS)coating on the poro...
详细信息
A facile modification strategy is developed to promote the proliferation and osteogenic differentiation of rat bone marrow stromal cells(rBMSCs)through deposition of a bioactive calcium silicate(CS)coating on the porous surface of poly(ether-ether-ketone)(PEEK)with the assistance of poly(dopamine)(PDA).The porous structures are etched on the surface of PEEK after sulfonation treatment.A poly(dopamine)layer is coated on the porous surface of the sulfonated PEEK(SPEEK),which provides anchoring groups for the subsequent deposition of the CS *** show that the CS coating on the porous surface of SPEEK significantly improve the hydrophilicity and biomineralization formation of *** with PEEK,SPEEK-PDA-CS displays higher bioactivity to promote the proliferation and osteogenic differentiation of rBMSCs,including the increase of ALP activity and formation of calcium nodules,the expression of osteogenic differentiation-related *** results are beneficial to extending clinical applications of PEEK-based implants for bone tissue repair and orthopedic surgery.