A novel process was introduced in this paper for the diameter-controlling synthesis of carbon nanofibers (CNFs) in the ethanol flames. The carbon nanofibers were grown on a nanocrystalline Fe layer, which was electro-...
A novel process was introduced in this paper for the diameter-controlling synthesis of carbon nanofibers (CNFs) in the ethanol flames. The carbon nanofibers were grown on a nanocrystalline Fe layer, which was electro-deposited on a substrate using periodic reverse (P.R.) pulse plating. It was found that the quality of the plating nanocrystalline and the corresponding carbon nanofibers was related with two plating parameters: output pulse frequency ( f ) and duty cycle ( r ). In addition to that the straight and helical carbon nanofibers were selectively synthesized by addition of different additives in plating bath. In this paper, the base-growth mechanism of carbon nanofibers was clearly discussed.
Using the microwave sintering technology, the effects of phosphorus （P） additions on the microstructure and properties of the ultrafine WC-10Co alloys were investigated. The experimental results show that with only ...
详细信息
Using the microwave sintering technology, the effects of phosphorus （P） additions on the microstructure and properties of the ultrafine WC-10Co alloys were investigated. The experimental results show that with only 0.3wt% P additions, full density WC-10Co cermets were obtained at temperature of 1250℃, which is 70 ℃ lower than that of the undoped counterparts. Lower sintering temperature can result in finer WC grain growth; therefore, the P-doped WC-10Co alloys exhibited higher hardness than the undoped ones. But at the same time, P doping could lead to sacrifice of fracture toughness ofWC-10Co cemented carbides.
The effects of glass flit on the sintering and electric properties of PMN-PT textured ceramics were investigated. The glass frits, including PbO, Bi2O3 and ZnO, were selected since liquid phase sintering lowered the P...
详细信息
The effects of glass flit on the sintering and electric properties of PMN-PT textured ceramics were investigated. The glass frits, including PbO, Bi2O3 and ZnO, were selected since liquid phase sintering lowered the PMN-PT sintering temperature. The piezoelectric properties of PMN-PT ceramics with glass frit addition are strongly dependent on the densification. The addition of glass frits into PMN-PT matrix reduced the sintering temperature to 1 100℃ instead of 1 150 ℃ for samples without glass. The piezoelectric coefficients （d33） of PMN-PT textured ceramics achieved 568 pc/N with 1 wt% excess PbO.
Polycrystalline samples of Sm partially filled skutterudites SmyFexCo4-xSb12 were prepared by melting and Spark Plasma Sintering technique. The results of Rietveld refinement showed that the obtained SmyFexCo4-xSb12 s...
详细信息
Polycrystalline samples of Sm partially filled skutterudites SmyFexCo4-xSb12 were prepared by melting and Spark Plasma Sintering technique. The results of Rietveld refinement showed that the obtained SmyFexCo4-xSb12 samples possessed filled skutterudite structures. The thermal parameter （B） of Sm is larger than that of Sb, Fe, and Co, indicating that Sm ＂rattled＂ in Sb-icosahedron voids. The effects of filling atom Sm on thermoelectric properties of these compounds were investigated. With the increase of Sm filling fraction （y）, electrical conductivity decreased, Seebeck coefficient increased and had a maximum value when y was 0.38; thermal conductivity reduced and had a minimum value when y was 0. 32. At 750 K, the highest figure of merit of 0.68 was obtained for Sm0.32Fe1.47Co2.53Sb12.
作者：
CAO MingHe TIAN Wei LI MingFa SUN WenHua HU MingJi LIU HanXingState Key Laboratory of Advanced Technology for Materials Synthesis and Processing
Wuhan University of Technology Wuhan 430070 China State Key Laboratory of Advanced Technology for Materials Synthesis and Processing Wuhan University of Technology Wuhan 430070 China State Key Laboratory of Advanced Technology for Materials Synthesis and Processing Wuhan University of Technology Wuhan 430070 China State Key Laboratory of Advanced Technology for Materials Synthesis and Processing Wuhan University of Technology Wuhan 430070 China State Key Laboratory of Advanced Technology for Materials Synthesis and Processing Wuhan University of Technology Wuhan 430070 China State Key Laboratory of Advanced Technology for Materials Synthesis and Processing Wuhan University of Technology Wuhan 430070 China
The NaNbO3 powders were synthesized and their crystal structure changes were analyzed by ultrahigh pressure up to 6 *** results indicate that the pure NaNbO3 powders can be synthesized at 300℃ under a pressure of 4 G...
详细信息
The NaNbO3 powders were synthesized and their crystal structure changes were analyzed by ultrahigh pressure up to 6 *** results indicate that the pure NaNbO3 powders can be synthesized at 300℃ under a pressure of 4 GPa, to sig- nificantly restrain the Na element volatilization compared with the traditional syn- thesis method. It is found that the crystal structure of synthesized NaNbO3 changes from low symmetry to high symmetry with the increase of the pressure.
The spores of Ganoderma lucidum were ground and broken to ultrafine particles by high speed centrifugal shearing（HSCS） pulverizer. The characteristics of Ganoderma lucidum spores were analyzed by scanning electron m...
详细信息
The spores of Ganoderma lucidum were ground and broken to ultrafine particles by high speed centrifugal shearing（HSCS） pulverizer. The characteristics of Ganoderma lucidum spores were analyzed by scanning electron microscope （SEM）, Fourier transform infrared spectrophotometry （FTIR）. Ultraviolet-visible pectrophotometer was used to determine the extraction ratio of aqueous solubility polysaccharide between the raw and broken spores. The immunological function on the mice before and after the breaking of spores wan investigated. The experimental results show that after being ground, the sporoderm-broken ratio reachs 100%, the original active ingredients of ganoderma lucidum spores do not change, and the extraction ratio of aqueous solubility polysaccharide is greatly increased by 40.08%. The broken spores show much higher immunological activity comparing with original spores of Ganoderma lucidum.
A new compound,[Co（dien）2]（dienH3）（H3O）7[P2Mo5O23]2·14H2O, has been hydrothermallly synthesized by using Na2MoO4,CoCl2, H3PO4 and dien, and structurally characterized by elemental analysis, X-ray powder dif...
详细信息
A new compound,[Co（dien）2]（dienH3）（H3O）7[P2Mo5O23]2·14H2O, has been hydrothermallly synthesized by using Na2MoO4,CoCl2, H3PO4 and dien, and structurally characterized by elemental analysis, X-ray powder diffraction analysis, SEM, IR and TG analysis. The results show that the compound is composed of a polyanion [P2Mo5O23]2^12, complex [Co（dien）2]^2＋ cation, protonated [dienH3]^3＋ , and forteen crystallization water molecule.
WC-10Co nanocrystalline composite powders prepared by spray pyrogenation-continuous reduction and carburization technology were consolidated by vacuum sintering plus hot isostatic pressing （HIP）. Influences of carbo...
详细信息
WC-10Co nanocrystalline composite powders prepared by spray pyrogenation-continuous reduction and carburization technology were consolidated by vacuum sintering plus hot isostatic pressing （HIP）. Influences of carbon content on properties and microstructure of ultrafine WC-10Co cemented carbide were investigated. The results show that the relative density of the ultrafine WC-10Co cemented carbides can reach 99.72%, and the transverse rupture strength （TRS） was higher than 3 890 MPa, Rockwell A hardness （HRA） was higher than 92.5, the average grain size was less than 460 nm, when carbon content in nanocrystalline composite powder was 5.54wt% and the ball-milled time was 48 hours, ultrafine WC-10Co cemented carbide with excellent properties and homogeneous microstructure was obtained.
A ternary-layered carbide Ti2AlC material could be synthesized by spark plasma sintering（SPS） technology using elemental powder mixture of Ti, Al and active carbon. By means of XRD and SEM, phases were identified an...
详细信息
A ternary-layered carbide Ti2AlC material could be synthesized by spark plasma sintering（SPS） technology using elemental powder mixture of Ti, Al and active carbon. By means of XRD and SEM, phases were identified and microscopically evaluated. The experimental results show that the main phase in the product was fully crystallized Ti2AlC with small particle size when sintered at 1200℃. The synthesis temperature of SPS was 200-400℃ lower than that of hot pressing （HP） or hot isostatic pressing （HIP）. Through thermodynamics calculations, the mechanism of Ti2AlC was studied by calculating changes of Gibbs free energy of reactions.
Serial material model （Dilute model）and Limited Units （LU）method were employed to analyze the performance of binary piezo-composite *** reckoned electric potential deployments illustrated difference while the part...
详细信息
Serial material model （Dilute model）and Limited Units （LU）method were employed to analyze the performance of binary piezo-composite *** reckoned electric potential deployments illustrated difference while the particles were *** piezoelectricities were also calculated according to the model,and furthermore comparation suggested that small particles living in the tolerance improve the piezoelectricity of *** coinciding with analyses were processed simultaneously. Ceramics were milled for different time in order to control the concentration of particle *** results showed that the filled particles enhanced the piezoelectricity of binary piezo-composite system efficiently whereas too many chips deteriorated the performance of piezo-composites.