Fe-Ni-Al mixtures as hot-pressing sintering additive to Titanium diboride （TiB2） were studied. It is found that liquid alloy formed under high temperature hardly has effects on the densification behaviors of TiB2-in...
详细信息
Fe-Ni-Al mixtures as hot-pressing sintering additive to Titanium diboride （TiB2） were studied. It is found that liquid alloy formed under high temperature hardly has effects on the densification behaviors of TiB2-independent. Fe-Ni-Al additive just works as filler between TiB2 particles and does not change the TiB2-independent sintering behaviors. Pressing mode has a great effect on the liquid flowing between TiB2 particles. Multiple-steps pressing mode will give more time and space for the liquid flowing and improve the relative density of TiB2-Fe-Ni-Al cermet.
Nafion/Silicon oxide composite membranes were produced via in situ sol-gel reaction of tetraethylorthosilicate （TEOS） in Nafion membranes. The physicochemical properties of the membranes were studied by FT-IR,TG-DSC...
详细信息
Nafion/Silicon oxide composite membranes were produced via in situ sol-gel reaction of tetraethylorthosilicate （TEOS） in Nafion membranes. The physicochemical properties of the membranes were studied by FT-IR,TG-DSC and tensile strength. The results show that the silicon oxide is compatible with the Nation membrane and the thermo stability of Nation/Silicon oxide composite membrane is higher than that of Nation membrane. Furthermore, the tensile strength of Nation/Silicon oxide composite membrane is similar to that of the Nation membrane. The proton conductivity of Nation/Silicon oxide composite membrane is higher than that of Nation membrane. When the Nation/Silicon oxide composite membrane was employed as an electrolyte in H2/O2 PEMFC, a higher current density value （1 000 mA/cm^2 at 0.38 V） than that of the Nafion1135 membrane （100 mA/cm^2 at 0.04 V） was obtained at 110 ℃.
About 300 μm thickness uniform thermal barrier coatings （TBCs） were deposited on the 1Cr18Ni9Ti samples by solution precursor plasma spray （SPPS）.The analysis methods,such as TEM,SEM,and XRD were used to characte...
详细信息
About 300 μm thickness uniform thermal barrier coatings （TBCs） were deposited on the 1Cr18Ni9Ti samples by solution precursor plasma spray （SPPS）.The analysis methods,such as TEM,SEM,and XRD were used to characterize the coatings in the aspects of microstructure and phase *** samples were quenched from 1121 ℃ to room temperature by forced-air to measure the thermal cycling *** density were measured by means of water *** experimental results show that grain size of the SPPS TBCs is about 30 nm with desired tetragonal phase ZrO2,and the SPPS TBCs（with 16% porosity） consist of arcuate pores,gelatin and melted *** hardness of the coatings is HR45Y38.5 and bond strength between coatings and substrates is 24.2 *** thermal shock test show the coatings have a average life of 500 cycles which is about 2.5 times than that of conventional air plasma spray （APS） TBCs.
Various parameters in spark plasma sintering（SPS）,such as sintering temperature,holding time,heating rate,and pressure,were adopted to investigate their effects on the densification of pure SnO2 *** obtained experim...
详细信息
Various parameters in spark plasma sintering（SPS）,such as sintering temperature,holding time,heating rate,and pressure,were adopted to investigate their effects on the densification of pure SnO2 *** obtained experimental data show that the SPS process enhances *** high-density undoped SnO2 ceramics （96.6% of theoretical） was obtained at much lower temperature （1000℃）,within a much shorter time,compared to the conventional sintering *** high-density undoped SnO2 ceramics （96.6% of theoretical） were obtained by SPS,under the condition of temperature：1000℃,pressure：40MPa,heating-rate：200℃/min,and holding time：3min
The effects of different sintering addictives on the preparation of CaF2 transparent ceramics were studied. Transparent CaF2 ceramics were fabricated by vacuum sintering and hot isostatic pressing （HIP） method, usin...
详细信息
The effects of different sintering addictives on the preparation of CaF2 transparent ceramics were studied. Transparent CaF2 ceramics were fabricated by vacuum sintering and hot isostatic pressing （HIP） method, using CaF2 nanopowders synthesized by chemical precipitation method as raw materials. The nanopowders and transparent ceramics were studied using X-ray diffraction, transmission electron microscopy （TEM）, scanning electron microscopy （SEM） and spectrophotometer. The experimental results indicated that the obtained nanopowders presented normal distribution with grain size about 30 nm; transmittance of CaF2 transparent ceramics was 39% and 26% at 1100 nm for LiF and NaF as sintering addictives, respectively, with corresponding mean grain size 188 μm and 44 μm. Loss of transmission could be attributed to the residual closed porosity. Sintering mechanism was liquid-phase sintering at pre-stage, then solid-phase sintering at later stage, as well as solid solution of lithium ions and sodium ions in the CaF2 lattice structure.
Flame retardant epoxy resins were prepared by a simple mixed method using ammonium aluminum carbonate hydroxy hydrate （AACHH） as a halogen-free flame retardant. The prepared samples were characterized by X-ray diffr...
详细信息
Flame retardant epoxy resins were prepared by a simple mixed method using ammonium aluminum carbonate hydroxy hydrate （AACHH） as a halogen-free flame retardant. The prepared samples were characterized by X-ray diffraction, thermogravimetric and differential scanning calorimetry, scanning electron microscope and limiting oxygen index（LOI） experiments. Effects of AACHH content on LOI of epoxy resins/AACHH composite and flame retardant mechanism were investigated and discussed. Results show that AACHH exhibites excellent flame-retardant properties in epoxy resin（EP）. When the content of AACHH was 47.4%, the LOI of EP reached 32.2%. Moreover, the initial and terminal decomposition temperature of EP increased by 48 ℃ and 40 ℃, respectively. The flame retarded mechanism of AACHH is due to the synergic flame retardant effects of diluting, cooling, decomposition resisting and obstructing.
A series of samples of hexagonal boron nitride-aluminum nitride ceramic composites with different amounts of CaF2 as sintering aid were prepared by spark plasma sintered at 1700-1850 ℃ for 5 *** addition of CaF2 effe...
详细信息
A series of samples of hexagonal boron nitride-aluminum nitride ceramic composites with different amounts of CaF2 as sintering aid were prepared by spark plasma sintered at 1700-1850 ℃ for 5 *** addition of CaF2 effectively lowered the sintering temperature and promoted the densification of AlN-BN *** the increase of sintering temperature,the density increased,and the contiguity of AlN grains enhanced in AlN-BN *** conductivity of AlN-BN composites increased with the increase in CaF2 content and sintering temperature,and there is a maximum value of 78.6 W·m^-1·K^-1 when the sample with 3wt% CaF2 sintered at 1800 ℃.
Here, a new idea was proposed for template-free synthesis of hierarchical m-ZrO2 nanorods and ＂their＂ possible formation mechanism based on a series of chemical reactions by simple hydrothermal method. The tradition...
详细信息
Here, a new idea was proposed for template-free synthesis of hierarchical m-ZrO2 nanorods and ＂their＂ possible formation mechanism based on a series of chemical reactions by simple hydrothermal method. The traditional preparation methods of hierarchical ZrO2 nanorods involved inexpensive equipment, complicated process, and high production cost. The as-synthesized products composed of many nanorods with 180-200 nm in diameter and 5-7 μm in length. The fi nal product after annealing involved hierarchical monoclinic ZrO2（m-ZrO2） nanorods, namely, the big nanorod was made up of many small nanorods with 40-50 nm in diameter and 500-600 nm in length. The experimental results were useful in understanding the chemical properties of ZrB2 and ZrO2 and the design of the derivatives for m-ZrO2 nanomaterials.
A rapid-heating method in the absence of electric/magnetic field was achieved by introducing a self-propagating-combustion （SHS） as heating source. The effect of heating rate on the alumina grain growth was explored...
详细信息
A rapid-heating method in the absence of electric/magnetic field was achieved by introducing a self-propagating-combustion （SHS） as heating source. The effect of heating rate on the alumina grain growth was explored based on this rapid-heating method. Comparing with the alumina prepared by two different heating ratios （greater than 1 000 ℃/min in SItS and about 50 ℃/min in common pressureless sintering furnace）, it was revealed that the rapid heating could promote the grain growth greatly without pressure during sintering. However, if a pressure was applied simultaneously, the grain growth would be almost completely restrained. Since these observations are quite different from the expectation, a new grain growth model was proposed.
The residual stresses on the surface of the d ifferently ground and polished silicon nitride ceramics were measured using X-r ay diffraction and identified by *** effect of the residual stress on the be nding strengt...
详细信息
The residual stresses on the surface of the d ifferently ground and polished silicon nitride ceramics were measured using X-r ay diffraction and identified by *** effect of the residual stress on the be nding strength was *** investigations show that the grinding proces s can introduce subatantial tensile residual stresses up to 290MPa on the surfac e of silicon nitride ceramics,which has a significant effect on reducing the ben ding strength of the ceramics after ***,in comparison with the ceramic s with a rough surface,the ceramics with a mirror image surface may have a lower *** can smooth the residual *** we evaluate the qualit y of the ceramic components after grinding,we must take residual stress into con sideration. The grinding methods and grinding conditions must be carefully selec ted in order to get the favorite residual stress as well as the surface smoothne ss.