The B4C-ZrB2-SiC ternary composites with super hard and high toughness were obtained by arc melting in argon atmosphere. Microstructures were observed by SEM, and phase compositions were analyzed by XRD. The hardness ...
详细信息
The B4C-ZrB2-SiC ternary composites with super hard and high toughness were obtained by arc melting in argon atmosphere. Microstructures were observed by SEM, and phase compositions were analyzed by XRD. The hardness and fracture toughness of ternary composites are 28GPa and 4.5MPa-m1/2. The eutectic mole composition is 0.39B4C-0.25ZrB2-0.36SiC, and the eutectic lamellar microstructure is composed of B4C matrix with the lamellar ZrB2 and SiC grains.
Using steel slag and charcoal as raw materials, the steel slag/charcoal nano-/micro-composites with magnetic-resistance mixed loss mode were fabricated by a high-performance milling process, and then the composition, ...
详细信息
Using steel slag and charcoal as raw materials, the steel slag/charcoal nano-/micro-composites with magnetic-resistance mixed loss mode were fabricated by a high-performance milling process, and then the composition, phase structure, morphology, and electromagnetic (EM) characteristics of the products were characterized by XRD, EDS, SEM, and vector network analyzer, respectively. The results showed that EM characteristics of the products were strongly dependent on the content of the charcoal (WCharcoal). The real and imaginary parts of the permittivity of the steel slag/charcoal nano-/micro-composites significantly increased with the increasing WCharcoal. Among them, the steel slag/charcoal composites with WCharcoal=50wt% exhibited the best EM-wave absorption performance, with a maximum reflectivity value of -33.4dB, the effective bandwidth 15.2GHz(<-10dB) and 8.6 GHz (<-20 dB), respectively, which is a consequence of enhanced dielectric loss and a proper EM matching.
A novel way was used to prepare dense B4C ceramics at a lower temperature by reactive sintering from carbon and boron elemental powders. Spark Plasma Sintering (SPS) technique, a rapid and non-conventional powder cons...
详细信息
ISBN:
(纸本)9780470927151
A novel way was used to prepare dense B4C ceramics at a lower temperature by reactive sintering from carbon and boron elemental powders. Spark Plasma Sintering (SPS) technique, a rapid and non-conventional powder consolidation method, was employed. The densification, microstructure and mechanical property of the as-prepared B4C ceramics were investigated. The reactive sintering process could be divided into two stages, corresponding to synthesis (1300∼1700°C) and densification (1700∼1900°C), respectively. At those stages, boron first reacted with carbon to form B4C, and then the in-situ densification of the as-synthesized B4C occurred and was enhanced by increasing sintering temperature. B4C ceramics with grain size of several hundred nanometers and high densification (98%) were obtained at 1800°C, a lower sintering temperature as compared with general hot press. Due to the high densification and purity as well as fine texture, the SPS-sintered B4C ceramics had high Vickers hardness (48.8GPa), Young's modulus (264.5GPa), fracture toughness (3.9MPa·m1/2) and flexure strength (450MPa).
In the present work, tetragonal BaTiO3 particles down to 20 nm have been synthesized by low temperature aqueous co-precipitation method through composition control. Field emission scanning electron microscopy (FE-SEM)...
详细信息
In the present work, tetragonal BaTiO3 particles down to 20 nm have been synthesized by low temperature aqueous co-precipitation method through composition control. Field emission scanning electron microscopy (FE-SEM) images indicated that the precipitates contained fine (about 20-30 nm) faceted particles. The Raman spectra revealed that tetragonal phase appeared with the increase in Ba/Ti ratio in the precursor solution. The appearance of tetragonal phase in BaTiO3 nanoparticle was related with the lattice defect revealed by lattice parameter and lattice strain calculated by XRD results. The lattice defect can be modified through composition control.
The Fe2O3 nanoparticles activated V2O5 nanotubes were achieved via a hydrolysis method. The TEM and SEM images of the nanotubes indicated that the Fe2O3 nanoparticles with the particle size of about 15 nm were dispers...
详细信息
Nanocrystalline titanium dioxide powder was synthesized by in-flight oxidation of titanium dihydride （TiH2） powder in a thermal plasma jet. TiH2 powder was injected into the thermal plasma jet and allowed to react w...
详细信息
Nanocrystalline titanium dioxide powder was synthesized by in-flight oxidation of titanium dihydride （TiH2） powder in a thermal plasma jet. TiH2 powder was injected into the thermal plasma jet and allowed to react with oxygen injected downstream the jet. Characteriza- tion of the powder by various analytical tools indicated that the powder consisted of nano-sized titanium dioxide particles consisting predominantly of the anatase phase. It is suggested that the thermo-chemistry of the oxidation process contributes significantly to the formation of nano-sized titania. The large energy released during the oxidation process dissociates the TiO2 particles into TiO（g） and titanium vapour, which recombine downstream with oxygen and form nano particles of TiO2.
ZnO-B2O3-SiO2 additive with 0.55: 0.35: 0.10 molar ratio was added to Ba0.3Sr0.7TiO3 ceramics in order to lower the sintering temperature. The densification behavior, crystalline structure, microstructure, dielectric ...
详细信息
ZnO-B2O3-SiO2 additive with 0.55: 0.35: 0.10 molar ratio was added to Ba0.3Sr0.7TiO3 ceramics in order to lower the sintering temperature. The densification behavior, crystalline structure, microstructure, dielectric properties and breakdown strength of ceramics were studied. When 9 wt.% additive was mixed with pure Ba0.3Sr0.7TiO3 powder, the densification temperature of samples decreased from 1350°C to 1100°C compared with no additive system, and the sintered ceramics revealed dielectric properties at room temperature as follows: dielectric constant Εr = 413, dielectric loss tanδ = 0.00231 under 1 kHz and the breakdown strength Eb = 9.2 kV/mm.
Lead free textured K_(0.5)Na_(0.5)NbO_(3) piezoelectric ceramics have been prepared by reactive-templated grain growth method by using NaNbO_(3) with different morphologies as templates. The NaNbO_(3) template particl...
详细信息
ISBN:
(纸本)9781457711626
Lead free textured K_(0.5)Na_(0.5)NbO_(3) piezoelectric ceramics have been prepared by reactive-templated grain growth method by using NaNbO_(3) with different morphologies as templates. The NaNbO_(3) template particles with different edge length (10-20 (mu)m) and thickness (0.5-2.5 (mu)m) was synthesized through controlling Bi_(1.5)Na_(x-1.5)Nb_(x)O_(3x+3) precursor's layer numbers x from 2 to 6 by two-step molten salt methods. The crystalline phases and microstructure of textured K_(0.5)Na_(0.5)NbO_(3) were characterized by X-ray diffraction and scanning electron microscopy, respectively. It shows that all the K_(0.5)Na_(0.5)NbO_(3) ceramics are orthorhombic perovskite structure with {001} orientation. By using the template particles with a ratio of edge length to thickness (l/h)(velence)approx10, the textured ceramics with optimized piezoelectric properties was prepared. The results indicate that the enhanced properties of textured ceramics are concerned with the template morphology.
暂无评论