The precursor of M-type barium hexaferrite with iron excess, which the nominal composition was BaFe12.4O19.6, was prepared by a so-called co-dump coprecipitation method. The crystallization behavior of the precursor u...
详细信息
The precursor of M-type barium hexaferrite with iron excess, which the nominal composition was BaFe12.4O19.6, was prepared by a so-called co-dump coprecipitation method. The crystallization behavior of the precursor under the spark plasma sintering (SPS) conditions and the magnetic properties of the SPS samples were investigated. The results show that the samples obtained at 700-850°C were composed of single-phase M-type barium hexaferrite, and that the crystallization of intermediates such as BaFe2O4 and Y-Fe2O3 did not occur. The distribution of crystal grains obviously changed with the increase of temperature;the distribution was random at 700°C and became preferential orientation when the temperature was more than 700°C. The saturation magnetization significantly increased at 700°C and remained almost constant in the range of 750°C to 850°C. This accorded with the evolution characteristics of the phase composition of the SPS samples with the increase of temperature. The coercivity first increased and then decreased with the increase of the temperature, which was attributed to the corresponding increases in the content of M-type barium ferrite and the degree of preferential orientation of crystal grains.
Transparent Fe-doped In2O3 thin film was prepared by sol-gel method on (general) glass substrate. The structure, morphologies, transmission and magnetic properties of the sample have been characterized by X-ray diffra...
详细信息
Transparent Fe-doped In2O3 thin film was prepared by sol-gel method on (general) glass substrate. The structure, morphologies, transmission and magnetic properties of the sample have been characterized by X-ray diffraction, field emission scanning electron microscopy, UV-Vis spectroscopy and vibrating sample magnetometer. XRD result indicated that the sample was single cubic In2O3 phase. FE-SEM clearly showed that the film was homogenous and composed of refining grain with an average size of 14 nm. UV-Vis spectrum indicated that the transmittance of the film was higher than 80% in the visible light, and the Fe-doped In2O3 film arose the optical absorption spectrum red shift. VSM demonstrated the sample was (room temperature ferromagnetic.
The carbonyl iron/Al2O3 core-shell composite particles with different morphologies of nanoshells were prepared and the influences of the Al2O3 nanoshell morphologies on the properties of the carbonyl iron/Al2O3 core-s...
详细信息
The carbonyl iron/Al2O3 core-shell composite particles with different morphologies of nanoshells were prepared and the influences of the Al2O3 nanoshell morphologies on the properties of the carbonyl iron/Al2O3 core-shell composite particles were investigated. The results show that the shell morphologies of the carbonyl iron/Al2O3 core-shell composite particles strongly depend on the species of acid and pH value. Compared to the carbonyl iron particles, the anti-oxidation property, microwave electromagnetic parameters and mechanical properties of the composite particles are significantly improved, and the particles, uniform, compact and grain-like Al2O3 nanoshells are beneficial to improving the anti-oxidation property and decreasing permittivity with the retention of permeability, while fiber-like Al2O3 nanoshells are more advantageous to improving the interface compatibility between the particles and the matrix of the polymers, resulting in obvious increase of mechanical properties of their based absorbing coatings.
Tin dioxide based ceramics doped with ZnO, Sb2O3 and ZnO-Sb2O3 were prepared by the pressureless sintering. The relative density (ρr) was measured by the Archimedes method, the resistivity (R) was measured by the van...
详细信息
Tin dioxide based ceramics doped with ZnO, Sb2O3 and ZnO-Sb2O3 were prepared by the pressureless sintering. The relative density (ρr) was measured by the Archimedes method, the resistivity (R) was measured by the van der Pauw method, and the mi-crostructure and crystal structure were measured by scanning electron microscope. Then the internal relationship between the material and structure were analyzed. The results indicate that ZnO can improve the sintering characteristics of the material;the ρr increases and then decreases with the increase of ZnO, and the optimal content of ZnO is 1.0% (mole fraction, the same below). However, the ρr decreases with the increase of Sb2O3;the R decreases at first, and then increases and decreases at last. The ρr and R of the material are good when Sb2O3 content is 0.5%. The SnO2 based ceramic doped with 1.0% ZnO-0.5% Sb2O3 and sintered at 1400°C has high performance;the ρr is 97% and the R is 0.1099 Ω·cm.
Ga dopping GaxPb1-xTe(x=0.01-0.05) compounds were prepared by melting reaction method, and the in-c fluence of Ga content on the thermoelectric properties were investigated. The results showed that temperature dopende...
详细信息
Ga dopping GaxPb1-xTe(x=0.01-0.05) compounds were prepared by melting reaction method, and the in-c fluence of Ga content on the thermoelectric properties were investigated. The results showed that temperature dopendent carrier concentration increased and the hall mobility decreased with increasing Ga content, which indicated that the carrier scattering mechanism gradually changed from an acoustical scattering to the interaction between an acoustical phone and an ionized impurity scattering as x increased. All samples show n-type conduct and the absolute Seebeck coefficient values and the electric conductivity increase significantly with increasing Ga content.
The layered perovskite-type organic-inorganic hybrids (CnH2n+1NH3)2 MnCl4 (n=2, 4, 6, 8, 10, 12) were synthesized in solution and their structures were characterized. The results showed that the structures of the prod...
详细信息
The layered perovskite-type organic-inorganic hybrids (CnH2n+1NH3)2 MnCl4 (n=2, 4, 6, 8, 10, 12) were synthesized in solution and their structures were characterized. The results showed that the structures of the products were independent on the reaction initial temperature. The X-ray diffraction (XRD) patterns and the scanning electron microscopy (SEM) images of the products demonstrated that the hybrids crystallize very well and had typical layered structures. The interlayer distance of each hybrid was obtained from the XRD patterns. It was linear dependent on the carbon atom number in the organic chain and the organic chains interdigitated between the two adjacent inorganic sheets.
The solubility of layered perovskite-type organic-inorganic hybrids (CnH2n+1 NH3)2MCl4 (where M = Mn, Co, Cu, Zn;n = 2, 4, 6, 8, 10, 12) in seven kinds of solvent are obtained by atomic absorption spectrometry and tit...
详细信息
The solubility of layered perovskite-type organic-inorganic hybrids (CnH2n+1 NH3)2MCl4 (where M = Mn, Co, Cu, Zn;n = 2, 4, 6, 8, 10, 12) in seven kinds of solvent are obtained by atomic absorption spectrometry and titration method. The solvents are sherwood oil, cyclohexane, acetone, trichloromethane, DMF, methanol and water. The results show that the hybrids are prone to dissolve in polar solvent. This is attributed to the polarity of the hybrids. The hybrids disassembly dissolve when the interaction between the ammonium and the electron-donating group of the solvent is stronger than that between the organic and the inorganic parts in the hybrids. The series of M = Zn and Co have better solubility in the polar solvent than that of M = Mn and Cu and this is presumably because there are weaker interactions between the organic and inorganic parts in hybrids of M = Zn and Co.
In this paper, we presented a novel route for fabricating Ti 3SiC2-based and Ti3AlC2-based solid solutions with mixed powders of TiC/Ti/Si/Al in different molar ratios. The phase compositions of these solid solutions ...
详细信息
In this paper, we presented a novel route for fabricating Ti 3SiC2-based and Ti3AlC2-based solid solutions with mixed powders of TiC/Ti/Si/Al in different molar ratios. The phase compositions of these solid solutions were studied by XRD and the stoichiometrics of these compounds were determined to be Ti 2.63Si0.87Al0.13C2 and Ti 2.76Al0.78Si0.22C2 by EDS. We also investigated the electronic properties and mechanical properties of these two ceramics. The results showed that the dopants were not only beneficial to the fabrication of Ti3SiC2 and Ti3AlC2 but also improved the properties of these two ceramics.
Ca(Al1/2Nb1/2)O3 (CAN) and Ca(Fe 1/2Nb1/2)O3 (CFN) were prepared by solid reaction route. With the sintering temperature increased, the Q×f value of CAN changes from 7 200 to 17 500 GHz due to the changing of the...
详细信息
Ca(Al1/2Nb1/2)O3 (CAN) and Ca(Fe 1/2Nb1/2)O3 (CFN) were prepared by solid reaction route. With the sintering temperature increased, the Q×f value of CAN changes from 7 200 to 17 500 GHz due to the changing of the ordering degree, whereas, the dielectric constant and Q×f value of CFN decrease remarkably without structural changing. The reason of this phenomenon is that the difference in size of two B-site ions in CAN is larger than that in CFN. As a result, the ordering degree of CAN is more sensitive to the conditions of sample preparation, compared with CFN.